Cobalt Iron Vanadium Hysteresis Alloy 2J10 FeCoV Viclloy

2J10 Iron Cobalt Vanadium Hysteresis Alloy Round Bar for Hysteresis Motor Rotor

2J10 can be precipitation hardened. It has good plasticity, and could be cold processed by forging, rolling and drawing and cutting. Usually, 2J10 is applied to motor equipment, such as hysteresis motor, hysteresis brake, etc. Fe-Co-V hysteresis alloys have good plasticity before tempering. After cold rolling (or drawing) with 90% strain, excellent hysteresis properties and strong magnetic anisotropy can be obtained, i.e. longitudinal magnetic properties are better than transverse ones. Therefore, if the wire can be used as the rotor of hysteresis motor in the manufacturing process, its performance is better, and it has more development prospects.

The corrosion resistance of 2J10 is good and it does not rust in the atmosphere.

Chemical composition

Application

2J10 is used to produce high efficiency hysteresis motor rotor and hysteresis brake. 2J10 wire can be used to make weigand wire in weigand sensor.

Forms of supply

Strip: thickness ≥0.05mm

Round bar diameter ≥10mm

Wire: diameter ≥0.20mm

cobalt iron alloy

magnetic materials

Vanadium Hysteresis Cobalt Iron Alloy